Numerical investigation of pulsed welding on aluminum alloy with a dual-region laser source: Exploring non-equal pulse parameters
Piandoro Samuele, Fortunato Alessandro, Liverani Erica, Ascari Alessandro
Abstract. Laser welding is a widely employed technique in modern industry, valued for its ability to achieve high-speed and high-quality welds. However, the weld quality depends heavily on precise control of laser parameters, as improper settings can lead to common defects. For aluminium alloys, such as 6082, minimizing heat input and managing cooling rates are critical to prevent issues like solidification cracking and ensure consistent weld integrity. Pulsed laser sources, as opposed to continuous ones, offer the advantage of reducing thermal stresses while maintaining high penetration depths. This study numerically investigates a dual-region laser source operating in pulsed mode for micro-welding applications. The laser comprises a high-intensity core for deep keyhole formation and an outer ring designed to stabilize the molten pool. Using a Volume of Fluid-based simulation framework, various pulse strategies were evaluated and compared to a novel configuration where the core operates in pulsed mode while the ring remains continuous. The results show that traditional rectangular pulses produce the highest cooling rates, increasing the risk of solidification cracks. However, incorporating a cooling-down phase and ramping the pulse shape effectively reduces the cooling rate, resulting also in more homogeneous penetration depths. The constant base power from the outer ring further enhances this effect by preheating the material before the pulse and extending the solidification time afterward. This extended solidification time reduces cracking risk and improves surface roughness. The study concludes that controlling the pulse shape and utilizing a constant base power from the ring can significantly reduce the cooling rate—by up to 45%, depending on the pulse shape—thereby enabling high-speed, high-quality welding of aluminium alloys, which are traditionally difficult to weld due to their thermal sensitivity.
Keywords
Pulsed Laser Welding, Aluminum Alloy, Core and Ring Laser, Numerical Simulation, Pulse Shaping
Published online 5/7/2025, 11 pages
Copyright © 2025 by the author(s)
Published under license by Materials Research Forum LLC., Millersville PA, USA
Citation: Piandoro Samuele, Fortunato Alessandro, Liverani Erica, Ascari Alessandro, Numerical investigation of pulsed welding on aluminum alloy with a dual-region laser source: Exploring non-equal pulse parameters, Materials Research Proceedings, Vol. 54, pp 2130-2140, 2025
DOI: https://doi.org/10.21741/9781644903599-229
The article was published as article 229 of the book Material Forming
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 license. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.
References
[1] Katayama, S., Fundamentals and Details of Laser Welding, 1st ed., Topics in Mining, Metallurgy and Materials Engineering, Springer Singapore, Singapore, 2020. https://doi.org/10.1007/978-981-15-7933-2
[2] Cao, X., Wallace, W., Poon, C., and Immarigeon, J.-P., Research and Progress in Laser Welding of Wrought Aluminum Alloys. I. Laser Welding Processes, Mater. Manuf. Process. 18(1) (2003) 1-22. https://doi.org/10.1081/AMP-120017586
[3] Sánchez-Amaya, J.M., Delgado, T., González-Rovira, L., and Botana, F.J., Laser welding of aluminium alloys 5083 and 6082 under conduction regime, Appl. Surf. Sci. 255(23) (2009) 9512-9521. https://doi.org/10.1016/j.apsusc.2009.07.081
[4] Bergmann, J., Bielenin, M., Herzog, R., Hildebrand, J., Riedel, I., Schricker, K., Trunk, C., and Worthmann, K., Prevention of solidification cracking during pulsed laser beam welding, PAMM 17(1) (2017) 405-406. https://doi.org/10.1002/pamm.201710172
[5] Ploshikhin, V., Prikhodovsky, A., Ilin, A., et al., Influence of the Weld Metal Chemical Composition on the Solidification Cracking Susceptibility of AA6056-T4 Alloy, Weld World 50 (2006) 46-50. https://doi.org/10.1007/BF03263460
[6] Hekmatjou, H., and Naffakh-Moosavy, H., Hot cracking in pulsed Nd:YAG laser welding of AA5456, Opt. Laser Technol. 103 (2018) 22-32. https://doi.org/10.1016/j.optlastec.2018.01.020
[7] Von Witzendorff, P., Kaierle, S., Suttmann, O., and Overmeyer, L., Using pulse shaping to control temporal strain development and solidification cracking in pulsed laser welding of 6082 aluminum alloys, J. Mater. Process. Technol. 225 (2015) 162-169. https://doi.org/10.1016/j.jmatprotec.2015.06.007
[8] Zhang, P., Jia, Z., Zhishui, Y., Shi, H., Li, S., Wu, D., Yan, H., Ye, X., Chen, J., Wang, F., and Tian, Y., A review on the effect of laser pulse shaping on the microstructure and hot cracking behavior in the welding of alloys, Opt. Laser Technol. 140 (2021) 107094. https://doi.org/10.1016/j.optlastec.2021.107094
[9] Bergmann, J.P., Bielenin, M., Stambke, M., Feustel, T., Von Witzendorff, P., and Hermsdorf, J., Effects of Diode Laser Superposition on Pulsed Laser Welding of Aluminum, Phys. Procedia 41 (2013) 180-189. https://doi.org/10.1016/j.phpro.2013.03.068
[10] Nakashiba, S., Okamoto, Y., Sakagawa, T., Miura, K., Okada, A., and Uno, Y., Welding characteristics of aluminum alloy by pulsed Nd:YAG laser with pre-and post-irradiation of superposed continuous diode laser, in: International Congress on Applications of Lasers & Electro-Optics, Laser Institute of America, Orlando, Florida, USA, 2011, pp. 825-832. https://doi.org/10.2351/1.5062333
[11] A. Ascari, A. Fortunato, L. Orazi, G. Campana, The influence of process parameters on porosity formation in hybrid LASER-GMA welding of AA6082 aluminum alloy, Optics & Laser Technology, Volume 44, Issue 5, 2012, Pages 1485-1490, ISSN 0030-3992, https://doi.org/10.1016/j.optlastec.2011.12.014
[12] G. Tani, G. Campana, A. Fortunato, and A. Ascari, “The influence of shielding gas in hybrid LASER–MIG welding,” Applied Surface Science, vol. 253, no. 19, pp. 8050–8053, 2007, doi: 10.1016/j.apsusc.2007.02.144
[13] Wang, L., Yao, M., Gao, X., Kong, F., Tang, J., and Kim, M.J., Keyhole stability and surface quality during novel adjustable-ring mode laser (ARM) welding of aluminum alloy, Opt. Laser Technol. 161 (2023) 109202. https://doi.org/10.1016/j.optlastec.2023.109202
[14] Pamarthi, V.V., Sun, T., Das, A., and Franciosa, P., Tailoring the weld microstructure to prevent solidification cracking in remote laser welding of AA6005 aluminium alloys using adjustable ringmode beam, J. Mater. Res. Technol. 25 (2023) 7154-7168. https://doi.org/10.1016/j.jmrt.2023.07.154
[15] Lin, R., Wang, H., Lu, F., Solomon, J., and Carlson, B.E., Numerical study of keyhole dynamics and keyhole-induced porosity formation in remote laser welding of Al alloys, Int. J. Heat Mass Transf. 108 (2017) 244-256. https://doi.org/10.1016/j.ijheatmasstransfer.2016.12.019
[16] Lee, J., Jang, J., Park, J., and Lee, S.H., Numerical and experimental analysis on the effect of ring beam-driven flow in coaxial dual-beam laser welding of aluminum alloy, Int. Commun. Heat Mass Transf. 157 (2024) 107800. https://doi.org/10.1016/j.icheatmasstransfer.2024.107800
[17] M. Dal, R. Fabbro, “An overview of the state of art in laser welding simulation,” Optics & Laser Technology, Vol. 78, Part A, 2016, pp. 2-14. https://doi.org/10.1016/j.optlastec.2015.09.015
[18] Hirt, C.W., and Nichols, B.D., Volume of fluid (VOF) method for the dynamics of free boundaries, J. Comput. Phys. 39 (1981) 201-225. https://doi.org/10.1016/0021-9991(81)90145-5
[19] Cho, J.-H., and Na, S.-J., Implementation of real-time multiple reflection and Fresnel absorption of laser beam in keyhole, J. Phys. Appl. Phys. 39 (2006) 5372-5378. https://doi.org/10.1088/0022-3727/39/24/039
[20] Schulz, W., Simon, G., Urbassek, H.M., and Decker, I., On laser fusion cutting of metals, J. Phys. Appl. Phys. 20 (1987) 481-488. https://doi.org/10.1088/0022-3727/20/4/013