Assessment of the effect of different sand grading on strength properties of metakaolin blended cement mortar
Solomon Olalere AJAMU, Rasheed ABDULWAHAB, Emmanuel Olatunde IBIWOYE, Toheed Ayomide OYEBAMIJI, Ayomide Faith USMANF, Akinbobola Joseph AKINDEJOYE
Abstract. Aggregate size has effects on the properties of cement composite. However, determination of sand grading is not usually put in to consideration in producing cement mortars for different application. Effects of different sand grading on the strength properties of metakaolin blended cement mortar have also not been well evaluated. In this study, effect of sand grading on the mechanical properties of metakaolin blended cement mortar, towards ensuring the development of durable and sustainable cement composite was investigated. Kaolin was sourced from Oyo State, South-West Nigeria. It was calcinated at 700oC to form metakaolin (MK) and characterized using X-Ray Fluorescence to determine its oxide composition. A blended cement produced with 15 to 25% replacement of Portland Limestone Cement (PLC) with the MK was used to produce mortar with different sand grading of fine, medium and coarse. Workability tests were carried out on freshly prepared mortar specimen with the three different sand grading. Water absorption, compressive strength and flexural strength tests on the different mortar specimen were carried out at 7, 14, 21, and 28 days, respectively. The addition of SiO2, Al2O3 and Fe2O3 of MK was found to be 79.23%. The grading variation are; Fine Sand (0.053 mm to 0.212 mm), Medium Sand (0.212 mm to 0.600 mm) and Coarse Sand (0.600 mm and 2.00). Workability of the mortar decreases with increasing particle sizes of sand and percentage replacement of PLC with MK. Fine sand absorbed more water with the highest at 25% MK replacement. Mortars specimen produced with Medium sand gave the highest compressive strength (15.11, 14.89 and 15.56 N/mm2) and flexural strength (5.616, 6.181 and 5.828 N/mm2) respectively for each of the 15, 20 and 25% replacement with MK. This study recommends the application of mortar containing medium sized sand with 20% MK for construction purposes.
Keywords
Metakaolin, Sand Grading, Compressive Strength, Flexural Strength, Cement Mortar, Sustainability
Published online 3/25/2025, 10 pages
Copyright © 2025 by the author(s)
Published under license by Materials Research Forum LLC., Millersville PA, USA
Citation: Solomon Olalere AJAMU, Rasheed ABDULWAHAB, Emmanuel Olatunde IBIWOYE, Toheed Ayomide OYEBAMIJI, Ayomide Faith USMANF, Akinbobola Joseph AKINDEJOYE, Assessment of the effect of different sand grading on strength properties of metakaolin blended cement mortar, Materials Research Proceedings, Vol. 51, pp 58-67, 2025
DOI: https://doi.org/10.21741/9781644903537-7
The article was published as article 7 of the book Advances in Cement and Concrete
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 license. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.
References
[1] ACI Committee 211, Standard Practice for Selecting Proportions for Normal, Heavyweight, and Mass Concrete (ACI 211.1-91). American Concrete Institute. (2014)
[2] A. M. Neville, Properties of Concrete. Pearson Education. (2011).
[3] P. K. Metha and P. J. Monteiro, Concrete: Microstructure, Properties, and Materials. McGraw-Hill Education. (2014).
[4] R. Kumar and B. Bhattacharjee, Porosity, Pore Size Distribution and in-Situ Strength of Concrete. Cement and Concrete Research, 33 (2003) 155-164. https://doi.org/10.1016/S0008-8846(02)00942-0. https://doi.org/10.1016/S0008-8846(02)00942-0
[5] L. Bertolini, B. Elsener, P. Pedeferri, and R. B. Polder, Corrosion of Steel in Concrete: Prevention, Diagnosis, Repair. Wiley-VCH. (2004). https://doi.org/10.1002/3527603379. https://doi.org/10.1002/3527603379
[6] G. M. Idorn, Durability of Concrete Structures. CRC Press. (1997).
[7] J. Ambroise and J. Péra, Effects of Metakaolin on the Properties of Concrete. Cement and Concrete Research, 34 (2004) 1521-1528. https://doi.org/10.1016/j.cemconres.2004.04.035
[8] J. M. Justice and T. Ueda, Metakaolin: A Review of Its Use in Concrete. Cement and Concrete Composites, 33 (2011) 881-891. https://doi.org/10.1016/j.cemconcomp.2011.02.011
[9] E. Badogiannis and S. Tsivilis, Exploitation of Poor Kaolin Deposits by Calcination. Cement and Concrete Research, 39 (2009) 1019-1026.
[10] J. M. Shilstone, Concrete Mixture Optimization. Concrete International, 12 (1990) 33-40.
[11] ASTM C618, Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. (2008).
[12] BS 3148, British Standard Methods of Test for Water for Making Concrete (including Notes on the Suitability of the Water). (1970).
[13] BS EN 196-1, Method of Testing Cement. (1995).
[14] BS1881-116, Method for determination of compressive strength of concrete. (1983).
[15] BS 1881- 118, Method for determination of flexural strength of concrete. (1983).
[16] BS 1881-102, Testing Concrete – Part 102: Method for Determination of Slump. British Standards Institution, London, UK. (1983).
[17] BS 1881-103, Testing Concrete – Part 103: Method for Determination of Compacting Factor. British Standards Institution, London, UK. (1983).
[18] ASTM C618-19, Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. ASTM International, West Conshohocken, PA. (2019).
[20] S. Wild, J. M. Khatib and A. Jones, Relative strength, pozzolanic activity and cement hydration in superplasticised metakaolin concrete. Cement and Concrete Research, 26 (1996) 1537-1544. https://doi.org/10.1016/0008-8846(96)00148-2